| 1. Identificação | ||||
| Tipo de Referência | Artigo em Revista Científica (Journal Article) | |||
| Site | mtc-m21c.sid.inpe.br | |||
| Código do Detentor | isadg {BR SPINPE} ibi 8JMKD3MGPCW/3DT298S | |||
| Identificador | 8JMKD3MGP3W34R/3UMEEB5 | |||
| Repositório | sid.inpe.br/mtc-m21c/2020/01.03.16.44 (acesso restrito) | |||
| Última Atualização | 2020:01.03.16.44.55 (UTC) simone | |||
| Repositório de Metadados | sid.inpe.br/mtc-m21c/2020/01.03.16.44.55 | |||
| Última Atualização dos Metadados | 2022:01.04.01.34.55 (UTC) administrator | |||
| DOI | 10.1016/j.materresbull.2019.110642 | |||
| ISSN | 0025-5408 1873-4227 | |||
| Chave de Citação | PereiraAlmeCoutFerr:2020:TiDiCa | |||
| Título | Titanium dioxide/oxidized carbon fiber electrodes electrochemically produced and their influences on Brilliant Green dye degradation  | |||
| Ano | 2020 | |||
| Mês | Feb. | |||
| Data de Acesso | 10 maio 2024 | |||
| Tipo de Trabalho | journal article | |||
| Tipo Secundário | PRE PI | |||
| Número de Arquivos | 1 | |||
| Tamanho | 2788 KiB | |||
| 2. Contextualização | ||||
| Autor | 1 Pereira, Lânia Auxiliadora 2 Almeida, Dalva Alves de Lima 3 Couto, Andréa Boldarini 4 Ferreira, Neidenêi Gomes | |||
| Identificador de Curriculo | 1 2 3 4 8JMKD3MGP5W/3C9JHU3 | |||
| Grupo | 1 LABAS-COCTE-INPE-MCTIC-GOV-BR 2 LABAS-COCTE-INPE-MCTIC-GOV-BR 3 LABAS-COCTE-INPE-MCTIC-GOV-BR 4 LABAS-COCTE-INPE-MCTIC-GOV-BR | |||
| Afiliação | 1 Instituto Nacional de Pesquisas Espaciais (INPE) 2 Instituto Nacional de Pesquisas Espaciais (INPE) 3 Instituto Nacional de Pesquisas Espaciais (INPE) 4 Instituto Nacional de Pesquisas Espaciais (INPE) | |||
| Endereço de e-Mail do Autor | 1 lania.fisica@yahoo.com.br 2 dalva.almeida@inpe.br 3 4 neidenei.ferreira@inpe.br | |||
| Revista | Materials Research Bulletin | |||
| Volume | 122 | |||
| Páginas | e110642 | |||
| Nota Secundária | A1_INTERDISCIPLINAR A1_ENGENHARIAS_III A1_ENGENHARIAS_II A1_ENGENHARIAS_I A2_MATERIAIS B1_QUÍMICA B1_ODONTOLOGIA B1_GEOCIÊNCIAS B1_FARMÁCIA B1_ASTRONOMIA_/_FÍSICA | |||
| Histórico (UTC) | 2020-01-03 16:45:14 :: simone :: 2019 -> 2020 2020-01-03 16:45:14 :: simone -> administrator :: 2020 2022-01-04 01:34:55 :: administrator -> simone :: 2020 | |||
| 3. Conteúdo e estrutura | ||||
| É a matriz ou uma cópia? | é a matriz | |||
| Estágio do Conteúdo | concluido | |||
| Transferível | 1 | |||
| Tipo do Conteúdo | External Contribution | |||
| Tipo de Versão | publisher | |||
| Palavras-Chave | TiO2 Carbon fiber Composite materials Photoelectrocatalysis Dye degradation | |||
| Resumo | Electrochemical advanced oxidation processes to degrade organic pollutants require the study of new anode materials. Porous structure of three-dimensional oxidized carbon fibers (OCF) associated to titanium dioxide (TiO2) becomes an alternative since they can effectively improve the mass transport in their enlarged areas. TiO2/OCF electrodes were produced from an optimized OCF substrate evaluating the influence of oxygen functional groups on its surface in the TiCl3 anodic hydrolysis. From scanning electron microscopy, Raman analyzes, and electro/photoelectrochemical responses, a suitable TiO2/OCF composite was obtained from oxidized CF for 30 min. TiO2 presented several characteristic Raman bands of anatase modes at 150, 398, 511, and 620 cm−1 . To improve the TiO2 crystallinity, the samples were also heat-treated at 500 °C in an argon atmosphere for 2, 3, and 4 h. TiO2/OCF composite treated for 2 h presented the highest electrochemically active surface area and photoelectrochemical activity. This is due to its TiO2 rougher morphology with rounded nanoparticles presence on OCF surface. For Brilliant Green dye degradation, an electrolysis process was highly efficient at the current density of 10 mA cm−2 at 300 min of time treatment. Besides, TiO2/OCF composite under UV irradiation shows an electrolysis efficiency improvement presenting the highest kinetic rate associated to the additional % OH radical productions. | |||
| Área | FISMAT | |||
| Arranjo | urlib.net > BDMCI > Fonds > Produção anterior à 2021 > LABAS > Titanium dioxide/oxidized carbon... | |||
| Conteúdo da Pasta doc | acessar | |||
| Conteúdo da Pasta source | não têm arquivos | |||
| Conteúdo da Pasta agreement |
| |||
| 4. Condições de acesso e uso | ||||
| Idioma | en | |||
| Arquivo Alvo | Pereira_titanium.pdf | |||
| Grupo de Usuários | simone | |||
| Grupo de Leitores | administrator simone | |||
| Visibilidade | shown | |||
| Permissão de Leitura | deny from all and allow from 150.163 | |||
| Permissão de Atualização | não transferida | |||
| 5. Fontes relacionadas | ||||
| Unidades Imediatamente Superiores | 8JMKD3MGPCW/3ESR3H2 | |||
| Lista de Itens Citando | sid.inpe.br/bibdigital/2013/09.24.19.30 3 sid.inpe.br/mtc-m21/2012/07.13.14.56.52 1 | |||
| Divulgação | WEBSCI | |||
| Acervo Hospedeiro | urlib.net/www/2017/11.22.19.04 | |||
| 6. Notas | ||||
| Campos Vazios | alternatejournal archivingpolicy archivist callnumber copyholder copyright creatorhistory descriptionlevel e-mailaddress format isbn label lineage mark mirrorrepository nextedition notes number orcid parameterlist parentrepositories previousedition previouslowerunit progress project rightsholder schedulinginformation secondarydate secondarykey session shorttitle sponsor subject tertiarymark tertiarytype url | |||
| 7. Controle da descrição | ||||
| e-Mail (login) | simone | |||
| atualizar | ||||